POM 4010旭化成

POM 4010旭化成--4010 is a homopolymer product of polyformaldehyde (POM). It is available in North America, Africa and the Middle East, Europe or the Asia-Pacific region, and 4010 applications include engineering/industrial accessories, housing and automotive industries.

均聚的聚甲醛树脂

等级

2010, MG210, 3010, 4010, 4050, 4060, 4012, 5010, 5050, 7010, 7050, 7054, 9054, 3013A, 4013A, 5013A, GA510, GA520, GN705, LT802, LT804, LT805, LT200, FS410, LA543, LM511, LS701

 

 

预干燥条件

温度 (ºC)

80 - 90

时间 (小时)

3 - 4

注塑条件

树脂温度 (ºC)

190 - 210 (低于230)

模具温度 (ºC)

> 50

等级

3510, 4520, 5520, 7520, 8520, HC450, HC550, HC750, HC460, HC760, 7554, 3513, 4513, 4563, 7513, GN455, GN755, SG454, CF452, CF454, MT754, TFC64, LD755, LT350, LV450, LZ750, EF750, TFC64

均聚POM、共聚POM及加纤25%增强材料性能参数对比表：

性能指标

均聚POM

共聚POM

25%GFPOM

相对密度

1.43

1.41　

1.61　

吸水率，%

2.5

2.1

—　

成型收缩率，%

1.5～3

1.5～3.5

—

拉伸强度，MPa

70

62

130

断裂伸长率，%

40

60

—

弯曲强度，MPa

90

98

182

拉伸弹性模量，MPa

3160

2830

8300

弯曲弹性模量，MPa

2880

2600

7600

压缩强度，MPa

127　

110

-　

剪切强度，MPa

67

54

—

缺口冲击强度，（J/m）

76　

65

86

洛氏硬度

M94　

M80

—

摩擦因数

—

0.15

—

疲劳极限，MPa

35　

31　

—

热变形温度（1.82MPa），℃

110

124

163

长期使用温度，℃

80　

100　

—　

线膨胀系数，(×10K)

7.5

8.5

2.6

热导率[W/(m·K)]

0.23　

0.23

—　

体积电阻率，Ω·cm

10　

10

3.8×10

介电常数（10Hz）

3.8

2.7　

—　

介电损耗角正切值（10Hz）

0.005　

0.007

-　　

介电强度（kV/mm）

20　

20　

—