TPU名称为热塑性聚氨酯弹性体橡胶。主要分为有聚酯型和聚醚型之分，他硬度范围（60HA—85HD）、耐磨、耐油、透明、弹性好、在日用品、体育用品、玩具、装饰材料等领域得到广泛应用，无卤阻燃TPU还可以代替软质PVC以满足越来越多领域的环保要求
特点：LNP THERMOCOMP* PU FF-1006 是一种玻璃纤维填充聚氨酯。
· LNP THERMOCOMP PU TF006
LNP THERMOCOMP Compound PU TF006
Also known as:LNP Thermocomp Compound TF-1006 Product reorder name:TF006
LNP Thermocomp FF-1006 is a glass fiber filled Polyurethane.
Property
TYPICAL PROPERTIES(1)
MECHANICAL | Value | Unit | Standard | ||
Tensile Stress,yld,Type I,5mm/min | 500 | kgf/cm | ASTM D 638 | ||
Tensile Stress,brk,Type I,5mm/min | |||||
Tensile Strain,yld,Type I,5mm/min | 16.3 | % | |||
Tensile Strain,brk,Type I,5mm/min | 16 | ||||
Tensile Modulus,50mm/min | 15000 | ||||
Flexural Stress,brk,1.3mm/min,50mm span | 590 | ASTM D 790 | |||
Flexural Modulus,1.3mm/min,50mm span | 17300 | ||||
Tensile Stress,yield,5mm/min | 51 | MPa | ISO 527 | ||
Tensile Stress,break,5mm/min | |||||
Tensile Strain,yield,5mm/min | 15.5 | ||||
Tensile Strain,break,5mm/min | |||||
Tensile Modulus,1mm/min | 1800 | ||||
Flexural Modulus,2mm/min | 2180 | ISO 178 | |||
IMPACT | |||||
Izod Impact,unnotched,23℃ | NB178 | cm-kgf/cm | ASTM D 4812 | ||
Izod Impact,notched,23℃ | 52 | ASTM D 256 | |||
Instrumented Impact Energy @ peak,23℃ | 198 | cm-kgf | ASTM D 3763 | ||
Multiaxial Impact | 179 | ISO 6603 | |||
Izod Impact,unnotched 80*10*4 +23℃ | 131 | kJ/m | ISO 180/1U | ||
Izod Impact,notched 80*10*4 +23℃ | 41 | ISO 180/1A | |||
THERMAL | |||||
HDT,0.45 MPa,3.2mm,unannealed | 167 | ℃ | ASTM D 648 | ||
HDT,1.82 MPa,3.2mm,unannealed | 78 | ||||
CTE,-40℃ to 40℃,flow | 2.70E-05 | 1/℃ | ASTM E 831 | ||
CTE,-40℃ to 40℃,xflow | 1.30E-04 | 2.84E-05 | ISO 11359-2 | 1.31E-04 | |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | ISO 75/Bf | ||||
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 85 | ISO 75/Af | |||
PHYSICAL | |||||
Density | 1.47 | g/cm | ASTM D 792 | ||
Moisture Absorption,50% RH,24 hrs | 0.36 | ASTM D 570 | |||
Mold Shrinkage,flow,24 hrs(5) | 0.1-0.4 | ASTM D 955 | |||
Mold Shrinkage,xflow,24 hrs(5) | 0.5-0.8 | 0.15 | ISO 294 | 0.4 | ISO 1183 |
Moisture Absorption(23℃/50% RH) | 0.5 | ISO 62 | |||
Source GMD,last updated:2008/03/26 | |||||
Parameter Injection Molding | Value | Unit |
Drying Temperature | 95-105 | ℃ |
Drying Time | 2 | hrs |
Maximum Moisture Content | 0.03 | % |
Melt Temperature | 210 | |
Nozzle Temperature | 205-225 | |
Front-Zone 3 Temperature | 200-220 | |
Middle-Zone 2 Temperature | 195-215 | |
Rear-Zone 1 Temperature | 195-210 | |
Mold Temperature | 15-45 | |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Shot to Cylinder Size | 40-80 |
聚氨酯弹性体是弹性体中比较特殊的一大类，聚氨酯弹性体的硬度范围很宽，性能范围很宽，所以聚氨酯弹性体是介于橡胶和塑料的一类高分子材料。可加热塑化，化学结构上没有货很少交联，其分子基本上是线性的，然而却存在一定的物理交联，这类聚氨酯称为TPU