产品详情
DuraStar DS2010
热塑性聚酯
Eastman Chemical Company
产品说明：
Durastar DS2010 polymer contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. DS2010 has very good toughness as shown by Izod impact resistance. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS2010 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily and fills intricate molds. Under existing United States Food and Drug Administration (FDA) regulations, Durastar DS2010 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240. This product is certified to ANSI/NSF Standard 51.
DuraStar DS2010 物性表
| 基本信息 |
|
|---|
| 黄卡编号 | |
| 添加剂 | |
| 特性 | 抗撞击性，良好 可加工性，良好 快的成型周期 良好的流动性 耐化学性良好 清晰度，高 韧性良好 食品接触的合规性 脱模性能良好 外观良好
|
| 用途 | |
| 机构评级 | FDA 21 CFR 177.1240 NSF 51
|
| 外观 | |
| 形式 | |
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 |
|
|
|
| -- | 1.20 | g/cm | ASTM D792 |
| 23°C | 1.19 | g/cm | ISO 1183 |
| 收缩率 - 流动 (3.20 mm) | 0.20 到 0.60 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 (R 级, 23°C) | 105 |
| ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 |
|
|
|
| 屈服, 23°C | 46.0 | MPa | ASTM D638 |
| 屈服, 23°C | 47.0 | MPa | ISO 527-2 |
| 断裂, 23°C | 53.0 | MPa | ASTM D638 |
| 断裂, 23°C | 49.0 | MPa | ISO 527-2 |
| 伸长率 |
|
|
|
| 屈服, 23°C | 5.0 | % | ASTM D638 |
| 屈服, 23°C | 4.0 | % | ISO 527-2 |
| 断裂, 23°C | 310 | % | ASTM D638 |
| 断裂, 23°C | 210 | % | ISO 527-2 |
| 弯曲模量 |
|
|
|
| 23°C | 1900 | MPa | ASTM D790 |
| 23°C | 1750 | MPa | ISO 178 |
| 弯曲应力 |
|
|
|
| 23°C | 64.0 | MPa | ISO 178 |
| 屈服, 23°C | 67.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 |
|
|
|
| -40°C | 60 | J/m | ASTM D256 |
| 23°C | 370 | J/m | ASTM D256 |
| -40°C | 6.3 | kJ/m | ISO 180 |
| 23°C | 30 | kJ/m | ISO 180 |
| 无缺口悬臂梁冲击 |
|
| ASTM D4812 |
| -40°C | 无断裂 |
| ASTM D4812 |
| 23°C | 无断裂 |
| ASTM D4812 |
| 装有测量仪表的落镖冲击 |
|
|
|
| -40°C, Energy at Peak Load | 48.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 45.0 | J | ASTM D3763 |
| -40°C, 能量到力量峰值 | 55.0 | J | ISO 6603-2 |
| 23°C, 能量到力量峰值 | 71.0 | J | ISO 6603-2 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火 | 73.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, 未退火 | 65.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 66.0 | °C | ISO 75-2/A |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 表面电阻率 | 1.0E+17 | ohms | ASTM D257 |
| 体积电阻率 (23°C) | 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 1(23°C) | 17 | kV/mm | ASTM D149 |
| 介电常数 |
|
| ASTM D150 |
| 23°C, 1 kHz | 2.60 |
| ASTM D150 |
| 23°C, 10 kHz | 2.60 |
| ASTM D150 |
| 23°C, 100 kHz | 2.50 |
| ASTM D150 |
| 23°C, 1 MHz | 2.50 |
| ASTM D150 |
| 耗散因数 |
|
| ASTM D150 |
| 23°C, 1 kHz | 6.0E-3 |
| ASTM D150 |
| 23°C, 10 kHz | 0.012 |
| ASTM D150 |
| 23°C, 100 kHz | 0.015 |
| ASTM D150 |
| 23°C, 1 MHz | 0.015 |
| ASTM D150 |
| 耐电弧性 | 123 | sec | ASTM D495 |
| 漏电起痕指数 | 700 | V | ASTM D3638 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 (3.00 mm, AT) | V-2 |
| UL 94 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 透射率 |
|
| ASTM D1003 |
| 总计 | 91.0 | % | ASTM D1003 |
| 常规 | 89.0 | % | ASTM D1003 |
| 雾度 | 0.30 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 |
|
|---|
| 干燥温度 | 70.0 | °C |
|
| 干燥时间 | 3.0 | hr |
|
| 加工（熔体）温度 | 250 到 290 | °C |
|
| 模具温度 | 15.0 到 30.0 | °C |
|