ABS AF-312T，AF-312T韩国LG ，AF-312T
长期批发经销ABS AF-312T韩国LG
湘远塑胶原料有限公司货源充足，品种齐全，价格合理,量大从优,当天订货当天发货。本公司郑重承诺所供产品绝对原产原包!假一赔十!可随货免费提供原料认证报告;UL认证、FDA认证、材质证明、ISO，ASTM物性资料、ROHS(SGS)报告、物质安全资料表(MSDS)物性、报价、UL报告、RoSH标准、SGS检测报告等）....
LG Chemical AF312T ABS物性表
物理性能额定值 (公制)额定值 (英制)测试方法比重1.18 g/cc1.18 g/ccASTM D792处理0.0100.010Injection Molding线性成型收缩率,Flow0.0040 - 0.0070 cm/cm@Thickness 3.20 mm
0.0040 - 0.0070 in/in@Thickness 0.126 in
ASTM D955熔体流动速率52 g/10 min@Load 10.0 kg, Temperature 220 °C
52 g/10 min@Load 22.0 lb, Temperature 428 °F
ASTM D1238机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（R 级）104104ASTM D785抗张强度(屈服)42.2 MPa@Thickness 3.20 mm
6120 psi@Thickness 0.126 in
50 mm/min; ASTM D638伸长率 (断裂)25 %@Thickness 3.20 mm
25 %@Thickness 0.126 in
50 mm/min; ASTM D638屈服伸长率>= 5.0 %@Thickness 3.20 mm
>= 5.0 %@Thickness 0.126 in
50 mm/min; ASTM D638拉伸模量2.16 GPa@Thickness 3.20 mm
313 ksi@Thickness 0.126 in
1 mm/min; ASTM D638弯曲强度68.6 MPa@Thickness 6.40 mm
9960 psi@Thickness 0.252 in
15 mm/min; ASTM D790弯曲模量2.60 GPa@Thickness 6.40 mm
377 ksi@Thickness 0.252 in
15 mm/min; ASTM D790悬壁梁缺口冲击强度2.26 J/cm@Thickness 6.40 mm, Temperature 23.0 °C
4.22 ft-lb/in@Thickness 0.252 in, Temperature 73.4 °F
ASTM D256@Thickness 3.20 mm, Temperature 23.0 °C
5.14 ft-lb/in@Thickness 0.126 in, Temperature 73.4 °F
ASTM D256Izod Impact, Unnotched0.785 J/cm@Thickness 6.40 mm, Temperature -30.0 °C
1.47 ft-lb/in@Thickness 0.252 in, Temperature -22.0 °F
ASTM D256@Thickness 3.20 mm, Temperature -30.0 °C
1.47 ft-lb/in@Thickness 0.126 in, Temperature -22.0 °F
ASTM D256电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率1.00e+14 ohm-cm1.00e+14 ohm-cm@Thickness >=1.50 mm
15 - 30 sec@Thickness >=0.0591 in
@Thickness >=2.00 mm
15 - 30 sec@Thickness >=0.0787 in
@Thickness >=2.50 mm
15 - 30 sec@Thickness >=0.0984 in
@Thickness >=3.00 mm
60 - 120 sec@Thickness >=0.118 in
@Thickness 1.50 mm
>= 120 arcs@Thickness 0.0591 in
@Thickness 2.00 mm
>= 120 arcs@Thickness 0.0787 in
@Thickness 2.50 mm
>= 120 arcs@Thickness 0.0984 in
@Thickness 3.00 mm
>= 120 arcs@Thickness 0.118 in
@Thickness 6.40 mm
183 °F@Thickness 0.252 in
Unannealed; ASTM D648载荷下热变形温度(1.8 MPa)76.0 °C@Thickness 6.40 mm
169 °F@Thickness 0.252 in
Unannealed; ASTM D648维卡软化温度84.0 °C@Load 5.00 kg
183 °F@Load 11.0 lb
50°C/h; ASTM D1525UL RTI85.0 °C@Thickness >=1.50 mm
185 °F@Thickness >=0.0591 in
UL 746B@Thickness >=2.00 mm
185 °F@Thickness >=0.0787 in
@Thickness >=2.50 mm
185 °F@Thickness >=0.0984 in
@Thickness >=3.00 mm
185 °F@Thickness >=0.118 in
@Thickness >=1.50 mm
167 °F@Thickness >=0.0591 in
UL 746B@Thickness >=2.00 mm
167 °F@Thickness >=0.0787 in
@Thickness >=2.50 mm
167 °F@Thickness >=0.0984 in
@Thickness >=3.00 mm
167 °F@Thickness >=0.118 in
@Thickness >=1.50 mm
167 °F@Thickness >=0.0591 in
UL 746B@Thickness >=2.00 mm
167 °F@Thickness >=0.0787 in
@Thickness >=2.50 mm
167 °F@Thickness >=0.0984 in
@Thickness >=3.00 mm
167 °F@Thickness >=0.118 in
@Thickness >=1.50 mm
V-0@Thickness >=0.0591 in
@Thickness >=2.00 mm
V-0@Thickness >=0.0787 in
@Thickness >=2.50 mm
V-0@Thickness >=0.0984 in
@Thickness >=3.00 mm
V-0@Thickness >=0.118 in