| 性能项目 | 试验条件 | 测试方法 | 测试数据 |
| 比重 |
| ASTMD792 | 0.948 | g/cm3 |
| 密度 |
| ISO1183 | 0.950 | g/cm3 |
| DetergentResistance |
| UL2157 | f4 |
|
| DetergentResistance |
| UL749 | f3 |
|
| 弹性体 |
| TestMethod | NominalValue | Unit |
| 拉伸应力-横向流量(应变,23°C) |
| ASTMD412 | 9.00 | MPa |
| 拉伸应力-横向流量(应变,23°C) |
| ISO37 | 9.00 | MPa |
| 抗张强度-横向流量(断裂,23°C) |
| ASTMD412 | 20.7 | MPa |
| TensileStress-AcrossFlow(Break,23°C) |
| ISO37 | 20.7 | MPa |
| 伸长率-横向流量(断裂,23°C) |
| ASTMD412 | 610 | % |
| 伸长率-横向流量(断裂,23°C) |
| ISO37 | 610 | % |
| 撕裂强度-横向流量2(23°C) |
| ASTMD624 | 67.0 | kN/m |
| TearStrength-AcrossFlow3(23°C) |
| ISO34-1 | 67 | kN/m |
| CompressionSet4 | 70°C,22hr | ASTMD395B | 54 | % |
| CompressionSet4 | 125°C,70hr | ASTMD395B | 61 | % |
| 压缩变形4 | 70°C,22hr | ISO815 | 54 | % |
| 压缩变形4 | 125°C,70hr | ISO815 | 61 | % |
| 肖氏硬度(邵氏D,15秒,23°C) |
| ISO868 | 41 |
|
| 脆化温度 |
| ASTMD746 | -52.0 | °C |
| 脆化温度 |
| ISO812 | -52.0 | °C |
| RTIElec |
| UL746 | 85.0 | °C |
| RTIStr |
| UL746 | 85.0 | °C |
| 空气中拉伸强度的变化率(150°C,168hr) |
| ASTMD573 | -11 | % |
| 空气中拉伸强度的变化率(150°C,168hr) |
| ISO188 | -11 | % |
| 空气中极限伸长率的变化率(150°C,168hr) |
| ASTMD573 | -15 | % |
| ChangeinTensileStrainatBreakinAir(150°C,168hr) |
| ISO188 | -15 | % |
| ChangeinDurometerHardnessinAir(ShoreD,150°C,168hr) |
| ASTMD573 | 4.0 |
|
| ChangeinShoreHardnessinAir(ShoreD,150°C,168hr) |
| ISO188 | 4.0 |
|
| 拉伸强度的变化率 | 23°C,168hr,inAceticAcid | ASTMD471 | 0.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inCyclohexane | ASTMD471 | -2.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inDetergent(Tide),2.5% | ASTMD471 | 0.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inEthanol,95% | ASTMD471 | -3.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | 6.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inIsopropylAlcohol | ASTMD471 | 5.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inMethylethylketone | ASTMD471 | 3.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inSodiumChloride,15% | ASTMD471 | 4.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 4.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inSulfuricAcid,98% | ASTMD471 | -22 | % |
| 拉伸强度的变化率 | 23°C,168hr,inTrichloroethylene | ASTMD471 | 8.0 | % |
| 拉伸强度的变化率 | 100°C,168hr,inDeionizedWater | ASTMD471 | 3.0 | % |
| 拉伸强度的变化率 | 100°C,168hr,inIRM903Oil | ASTMD471 | -26 | % |
| 拉伸强度的变化率 | 125°C,70hr,inIRM903Oil | ASTMD471 | -27 | % |
| 拉伸强度的变化率 | 125°C,168hr,inIRM903Oil | ASTMD471 | -30 | % |
| 拉伸强度的变化率 | 23°C,168hr,inAceticAcid | ISO1817 | 0.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inCyclohexane | ISO1817 | -2.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inDetergent(Tide),2.5% | ISO1817 | 0.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inEthanol,95% | ISO1817 | -3.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inHydrochloricAcid,10% | ISO1817 | 6.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inIsopropylAlcohol | ISO1817 | 5.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inMethylethylketone | ISO1817 | 3.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inSodiumChloride,15% | ISO1817 | 4.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | 4.0 | % |
| 拉伸强度的变化率 | 23°C,168hr,inSulfuricAcid,98% | ISO1817 | -22 | % |