PC/ABS合金料FR3009工厂直营

拜耳 FR3009 PC / ABS共混物 类别：聚合物；热塑性的；聚合物；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC） 材料说明：（PC+ABS）混合；阻燃剂；维卡/ B 120温度为103°C；UL认证94 5VB 1.8毫米；FR3000 bbs066接班人；改进的抗水解性能

物性表：

Physical PropertiesMetricEnglishCommentsDensity 1.18 g/cc0.0426 lb/in³ISO 1183-1Moisture Absorption at Equilibrium 0.20 %0.20 %ISO 62, 50% RHWater Absorption at Saturation 0.50 %0.50 %ISO 62Viscosity 150000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C150000 cP
@Shear Rate 1000 1/s,
Temperature 500 °Fmelt viscosity; b.o. ISO 11443-ALinear Mold Shrinkage, Flow 0.0045 - 0.0065 cm/cm
@Thickness 3.00 mm0.0045 - 0.0065 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577Linear Mold Shrinkage, Transverse 0.0045 - 0.0065 cm/cm
@Thickness 3.00 mm0.0045 - 0.0065 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577Melt Flow 29.5 g/10 min
@Load 5.00 kg,
Temperature 240 °C29.5 g/10 min
@Load 11.0 lb,
Temperature 464 °FISO 1133
Mechanical PropertiesMetricEnglishCommentsTensile Strength at Break 50.0 MPa7250 psi50 mm/min; ISO 527-1,-2Tensile Strength, Yield 60.0 MPa8700 psi50 mm/min; ISO 527-1,-2Elongation at Break >= 50 %>= 50 %50 mm/min; b.o. ISO 527-1,-2Elongation at Yield 4.0 %4.0 %50 mm/min; ISO 527-1,-2Tensile Modulus 2.80 GPa406 ksi1 mm/min; ISO 527-1,-2Izod Impact, Notched (ISO)  8.00 kJ/m²
@Temperature -30.0 °C3.81 ft-lb/in²
@Temperature -22.0 °FISO 180-A
12.0 kJ/m²
@Temperature 23.0 °C5.71 ft-lb/in²
@Temperature 73.4 °FISO 180-AIzod Impact, Unnotched (ISO) NB
@Temperature 23.0 °CNB
@Temperature 73.4 °FISO 180-U
Electrical PropertiesMetricEnglishCommentsVolume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093Surface Resistance 1.00e+16 ohm1.00e+16 ohmIEC 60093Dielectric Constant  3.1
@Frequency 100 Hz3.1
@Frequency 100 HzIEC 60250
3.1
@Frequency 1.00e+6 Hz3.1
@Frequency 1.00e+6 HzIEC 60250Dielectric Strength 30.0 kV/mm
@Thickness 1.00 mm762 kV/in
@Thickness 0.0394 inIEC 60243-1Dissipation Factor  0.0050
@Frequency 100 Hz0.0050
@Frequency 100 HzIEC 60250
0.0070
@Frequency 1.00e+6 Hz0.0070
@Frequency 1.00e+6 HzIEC 60250Comparative Tracking Index 300 V300 VSolution A; IEC 60112
Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 75.0 µm/m-°C
@Temperature 23.0 - 55.0 °C41.7 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2CTE, linear, Transverse to Flow 75.0 µm/m-°C
@Temperature 23.0 - 55.0 °C41.7 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C203 °FISO 75-1,-2Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C185 °FISO 75-1,-2Vicat Softening Point  101 °C
@Load 5.10 kg214 °F
@Load 11.2 lb50°C/h; ISO 306
103 °C
@Load 5.10 kg217 °F
@Load 11.2 lb120°C/h; ISO 306Flammability, UL94  V-0
@Thickness 1.50 mmV-0
@Thickness 0.0591 in

5VB
@Thickness 1.80 mm5VB
@Thickness 0.0709 inUL 94-5V
5VA
@Thickness 3.00 mm5VA
@Thickness 0.118 inUL 94-5V
Processing PropertiesMetricEnglishCommentsMelt Temperature 240 °C464 °FInjection molding; ISO 294Mold Temperature 80.0 °C176 °FInjection molding; ISO 294Injection Velocity 240 mm/sec9.45 in/secISO 294