SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC 物性

Polymer,Thermoplastic,Polycarbonate (PC),Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced,Polyester, TP,Polybutylene Terephthalate (PBT) SABIC Innovative Plastics (GE Plastics) 产品说明:

Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybutylene terephthalate) resin with excellent low temperature impact and chemical resistance. Range gray, black and colors except bright whites. Post-consumer usage: Each 1kg of Xenoy iQ1103 resin is made from approximately 0.33 kg of post-consumer content.

比重	1.19 g/cc	1.19 g/cc	ASTM D792
密度	1.20 g/cc	0.0434 lb/in³	ISO 1183
水分吸收	0.0800 %	0.0800 %	23°C / 50% RH; ISO 62
饱和吸水率	0.30 %	0.30 %	ISO 62
线性成型收缩率,Flow	0.0080 - 0.012 cm/cm @Thickness 3.20 mm	0.0080 - 0.012 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	13 g/10 min @Load 5.00 kg, Temperature 250 °C	13 g/10 min @Load 11.0 lb, Temperature 482 °F	ASTM D1238
化合物熔体指数	12 g/10 min @Load 5.00 kg, Temperature 250 °C	12 g/10 min @Load 11.0 lb, Temperature 482 °F	MVR [cm^3/10 min]; ISO 1133

机械性能 额定值 (公制) 额定值 (英制) 测试方法

抗张强度(断裂)	46.0 MPa	6670 psi	Type I, 50 mm/min; ASTM D638
	47.0 MPa	6820 psi	50 mm/min; ISO 527
抗张强度(屈服)	45.0 MPa	6530 psi	Type I, 50 mm/min; ASTM D638
	49.0 MPa	7110 psi	50 mm/min; ISO 527
伸长率 (断裂)	140 %	140 %	Type I, 50 mm/min; ASTM D638
	150 %	150 %	50 mm/min; ISO 527
屈服伸长率	4.0 %	4.0 %	Type I, 50 mm/min; ASTM D638
	4.0 %	4.0 %	50 mm/min; ISO 527
拉伸模量	1.95 GPa	283 ksi	1 mm/min; ISO 527