PC-ABS高流动C1110

PC-ABSC1110，高流动PC-ABS，高流动C1110   PC-ABS高流动C1110

SABIC Innovative Plastics Cycoloy® C1110 PC+ABS 物性表

物理性能额定值 (公制)额定值 (英制)测试方法比重1.14 g/cc1.14 g/ccASTM D792吸水率0.10 %

@Time 86400 sec

0.10 %

@Time 24.0 hour

ASTM D570平衡吸湿0.40 %0.40 %ASTM D570线性成型收缩率,Flow0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm

0.0050 - 0.0070 in/in

@Thickness 0.126 in

SABIC Method熔体流动速率2.5 g/10 min

@Load 3.80 kg, Temperature 230 °C

2.5 g/10 min

@Load 8.38 lb, Temperature 446 °F

ASTM D1238
8.0 g/10 min

@Load 3.80 kg, Temperature 260 °C

8.0 g/10 min

@Load 8.38 lb, Temperature 500 °F

ASTM D1238机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(屈服)56.0 MPa8120 psiType I, 50 mm/min; ASTM D638伸长率 (断裂)150 %150 %Type I, 50 mm/min; ASTM D638屈服伸长率5.0 %5.0 %Type I, 50 mm/min; ASTM D638拉伸模量2.20 GPa319 ksi50 mm/min; ASTM D638弯曲强度86.0 MPa12500 psi1.3 mm/min, 50 mm span; ASTM D790弯曲模量2.34 GPa339 ksi1.3 mm/min, 50 mm span; ASTM D790悬壁梁缺口冲击强度6.40 J/cm12.0 ft-lb/inASTM D256
5.34 J/cm

@Temperature -30.0 °C

10.0 ft-lb/in

@Temperature -22.0 °F

ASTM D256Dart Drop, Total Energy40.0 J

@Temperature -30.0 °C

29.5 ft-lb

@Temperature -22.0 °F

ASTM D3763
54.0 J

@Temperature 23.0 °C

39.8 ft-lb

@Temperature 73.4 °F

ASTM D3763电气性能额定值 (公制)额定值 (英制)测试方法耐电弧性120 - 180 sec120 - 180 secTungsten; ASTM D495相比耐漏电起痕指数(CTI)175 - 250 V175 - 250 VUL 746A热丝引燃 (HWI)15 - 30 sec15 - 30 secUL 746A高电弧燃烧，HAI>= 120 arcs>= 120 arcsUL 746A高压电弧跟踪率，HVTR10.0 - 25.4 mm/min0.394 - 1.00 in/minUL 746A热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C

40.0 µin/in-°F

@Temperature -40.0 - 104 °F

ASTM E 831导热系数0.200 W/m-K1.39 BTU-in/hr-ft²-°FASTM C177载荷下热变形温度(0.46 MPa)123 °C

@Thickness 3.20 mm

253 °F

@Thickness 0.126 in

unannealed; ASTM D648载荷下热变形温度(1.8 MPa)107 °C

@Thickness 3.20 mm

225 °F

@Thickness 0.126 in

unannealed; ASTM D648UL RTI60.0 °C140 °FUL 746BUL RTI，机械冲击60.0 °C140 °FUL 746BUL RTI，机械无冲击60.0 °C140 °FUL 746B可燃性(UL94)HB

@Thickness 1.21 mm

HB

@Thickness 0.0476 in

UL 94材料描述
测试方法UV-light, water exposure/immersionF2UL 746C