拉伸冲击试验机 塑料拉伸冲击性能试验方法

XJL数显拉伸冲击试验机

一 产品介绍

   主要用于在规定的拉伸冲击速度下，测定塑料试样断裂所需能量的测试。 用于测定塑料等非金属材料的脆性、韧性。

特点

仪器具有中英文操作界面，支持国标和美标试样检测，触摸屏操作，带微打印，自动计算冲击强度，独有USB接口，可连接电脑，操作简单。

三符合标准：

GB/T 13525-92《塑料拉伸冲击性能试验方法》

ASTM D1822-2006《使塑料及电绝缘材料断裂所需的拉伸冲击能量的测试方法》

ISO 8256-2004《塑料-拉伸-冲击强度的测定》

四技术参数：

1冲击速度：3.8m/s　
2冲击能量：15J 25J
3摆锤力矩：pd15J=8.03848Nm pd25J=13.39746Nm
4摆锤预扬角：160°
5打击中心距：395mm
6使用温度：（15-35）℃
7试样尺寸：长度80±2mm 宽度15±0.5mm 厚度<4mm
8 夹具间的自由长度：30±2mm

9 电源： 220VAC-15%～220VAC+10% 50HZ （单相三线制）

10试样形状和尺寸：试样厚度优先选用1mm。由产品裁取的试样，保留原厚度；厚度大于4mm的试样应机械加工为4mm。对于很薄的薄膜，可以使用多层试样，但应重叠良好。

11选择合适的摆锤使冲击能量读数在试验机有效范围内，参照下表：

（在能夹紧试样的前提下尽量选择质量小的丁字头）

XJL digital stretch impact testing machine

A product introduction

It is mainly used to measure the energy required for the fracture of plastic samples at the prescribed tensile impact velocity.

Used to measure the brittleness and toughness of nonmetallic materials such as plastics.

feature

Using the round grating measuring Angle technology, it has the characteristics of high precision, good stability and wide range of measurement

It has the function of calculating the punching power, the impact strength and the average of a batch of samples

It is convenient to check the Angle of elevation and lift Angle

4 display mode: LCD

Three meets the standard:

Test methods of plastic stretch impact performance

ASTM d1822-2006 "test method for the tensile impact energy required to fracture the plastic and electrical insulating materials"

ISO 8256-2004 plastics - stretch - impact strength measurement

Technical parameters:

1 impact velocity: 3.8m/s

2 impact energy: 15J 25J

3 pendulum moment: pd15J=8.03848Nm pd25J=13.39746Nm

4 pendulum early Yang Angle: 160 °

5 striking center distance: 395mm

6 use temperature: 15 to 35 ℃

Sample size: length 80 + + 2mm width 15 plus or minus 0.5mm thickness<4mm

Free length between clamps: 30 + 2mm

9 power supply: 220VAC-15% ~ 220VAC+10% 50HZ (single-phase three-wire system)

10 sample shape and size: 1mm for sample thickness.

The sample made by the product shall retain the original thickness;

The specimen with thickness of more than 4mm shall be machined to 4mm.

For thin films, you can use multi-layer samples, but they should be well overlapped.

11. Select the appropriate pendulum to make the impact energy reading within the range of the test machine, and refer to the following table:

(try to choose a small "t-head" with a small quality when you can clamp the sample)

Pendulum impact energy J

g

15.0

30 + 1 or 60 plus or minus 1

60 + / - 1 or 120 + 1