| Tensile Strength at Break |
80.0MPa |
11600psi |
cond.; ISO 527-1, -2; 5 mm/min |
| |
130MPa |
18900psi |
d.a.m.; ISO 527-1, -2; 5 mm/min |
| Elongation at Break |
4.30 % |
4.30 % |
d.a.m.; ISO 527-1, -2; 5 mm/min |
| |
16.0 % |
16.0 % |
cond.; ISO 527-1, -2; 5 mm/min |
| Tensile Modulus |
3.40GPa |
493ksi |
cond.; ISO 527-1, -2; 1 mm/min |
| |
6.30GPa |
914ksi |
d.a.m.; ISO 527-1, -2; 1 mm/min |
| Flexural Modulus |
2.60GPa |
377ksi |
cond., 2 mm/min; ISO 178-A |
| |
5.40GPa |
783ksi |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Strength |
100MPa
@Strain 7.30 % |
14500psi
@Strain 7.30 % |
cond., 2 mm/min; ISO 178-A |
| |
205MPa
@Strain 6.00 % |
29700psi
@Strain 6.00 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Yield Strength |
75.0MPa
@Strain 3.50 % |
10900psi
@Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| |
175MPa
@Strain 3.50 % |
25400psi
@Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A |
| Izod Impact, Unnotched (ISO) |
42.0kJ/m2
@Temperature -30.0 °C |
20.0ft-lb/in2
@Temperature -22.0 °F |
d.a.m.; ISO 180-1U |
| |
55.0kJ/m2
@Temperature 23.0 °C |
26.2ft-lb/in2
@Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
| |
75.0kJ/m2
@Temperature 23.0 °C |
35.7ft-lb/in2
@Temperature 73.4 °F |
cond.; ISO 180-1U |
| Charpy Impact Unnotched |
4.50J/cm2
@Temperature -30.0 °C |
21.4ft-lb/in2
@Temperature -22.0 °F |
d.a.m.; ISO 179-1eU |
| |
6.00J/cm2
@Temperature 23.0 °C |
28.6ft-lb/in2
@Temperature 73.4 °F |
d.a.m.; ISO 179-1eU |
| Charpy Impact, Notched |
<=1.00J/cm2
@Temperature 23.0 °C |
<=4.76ft-lb/in2
@Temperature 73.4 °F |
d.a.m.; ISO 179-1eA |
| |
<=1.00J/cm2
@Temperature -30.0 °C |
<=4.76ft-lb/in2
@Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| |
<=1.00J/cm2
@Temperature -30.0 °C |
<=4.76ft-lb/in2
@Temperature -22.0 °F |
cond.; ISO 179-1eA |
| |
1.20J/cm2
@Temperature 23.0 °C |
5.71ft-lb/in2
@Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Izod Impact, Notched (ISO) |
<=10.0kJ/m2 |
<=4.76ft-lb/in2 |
d.a.m.; ISO 180-1A |
| |
10.0kJ/m2 |
4.76ft-lb/in2 |
cond.; ISO 180-1A |
| |
| Surface Resistance |
1.00e+11ohm |
1.00e+11ohm |
d.a.m.; IEC 60093 |
| Comparative Tracking Index |
375V |
375V |
d.a.m.; Solution A; IEC 60112 |
| |
| CTE, linear, Parallel to Flow |
40.0μm/m-°C
@Temperature 23.0 - 55.0 °C |
22.2μin/in-°F
@Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow |
100μm/m-°C
@Temperature 23.0 - 55.0 °C |
55.6μin/in-°F
@Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point |
262°C |
504°F |
10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) |
245°C |
473°F |
ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) |
225°C |
437°F |
ISO 75-1, -2 |
| Vicat Softening Point |
255°C
@Load 5.10 kg |
491°F
@Load 11.2 lb
|
|