产品说明

dupont™ teflon® pfa 340 is a general-purpose resin available in clear, 2.5-mm (0.1-in.) pellets. compared with other grades of teflon® pfa, its most unique features are a relatively high flow rate and properties that make it suitable for a variety of processes and demanding end uses.

teflon® pfa 340 and the other teflon® pfa (perfluoroalkoxy) fluoropolymer resins combine the processing ease of conventional thermoplastics with properties similar to those of polytetrafluoroethylene. they have high melt strength, stability at high processing temperatures, and resistance to creep at high service temperature.

teflon® pfa 340 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoropolymer resin. for a given process, its high melt strength and thermal stability can be used to improve rates. compared with other fluoropolymers, its creep resistance at its high service temperatures provides a superior balance and level of end-use properties.

properly processed products made from neat teflon® pfa 340 resin provide the superior properties typical of the fluoropolymer resins: retention of properties after service at 260°c (500°f), useful properties at -196°c (-320°f), and chemical inertness to nearly all industrial chemicals and solvents. dielectric constant and dissipation factor are exceptionally low. molded products have moderate stiffness and high ultimate elongation.

in a flame situation, products of teflon® pfa 340 resist ignition and do not themselves promote flame spread. when ignited by flame from other sources, their contribution of heat is small and with very little smoke.

statements, or data, regarding behavior in a flame situation are not intended to reflect hazards presented by this or any other material when under actual fire conditions.

总体

材料状态      •已商用：当前有效                 

供货地区      •北美洲      •欧洲          

      •南美洲      •亚太地区          

      •刚性，良好      •良好的熔体强度      •耐气候影响性能良好      

性能特点      •抗溶解性   •流动性高   •烟释放，低      

      •良好的抗蠕变性      •耐化学性良好   •延展性，高      

用途      •薄膜   •工业领域：      •管道   

      •电器导线绝缘材料   •管道   •型材   

外观      •清晰/透明                

形式      •颗粒料                    

加工方法      •挤出   •压缩模塑          

      •树脂传递成型   •注射成型          

物理性能             额定值单位制      测试方法      

比重              2.14g/cm³      astm d792  

熔流率(372°c/5.0 kg)             14g/10 min     astm d1238

吸水率(24 hr)             0.030%   astm d570  

机械性能             额定值单位制      测试方法      

抗张强度                     astm d638  

屈服, 23°c          13.8mpa       

23°c              24.8mpa       

250°c            12.4mpa       

伸长率                  astm d638  

断裂, 23°c          300%            

断裂, 250°c        480%            

弯曲模量                     astm d790  

23°c              586mpa        

250°c            55.2mpa       

硬度             额定值单位制      测试方法      

硬度计硬度(邵氏d)         55    astm d2240

热性能          额定值单位制      测试方法      

熔融温度              302到310°c           

线形膨胀系数-流动                astm d696  

21到100°c              0.00014cm/cm/°c             

100到149°c            0.00017cm/cm/°c             

149到209°c            0.00021cm/cm/°c             

1 / 2                     

teflon® pfa 340          2012年9月30日

全氟烷氧基          

dupont fluoropolymers       

电气性能      额定值单位制      测试方法

体积电阻率    1.0e+18ohm•cm    astm d257

介电强度2 (0.254 mm)       79kv/mm       astm d149

介电常数              astm d150

60 hz      2.03

1 mhz    2.03

耗散因数              astm d150

60 hz      0.00010  

1 mhz    0.00010  

可燃性   额定值单位制      测试方法

极限氧指数    95% astm d2863

补充信息             

specific gravity, astm d792: 2.12 to 2.17       

mit folding endurance, 0.18 to 0.2mm (0.007 to 0.008 in): 15000 cycles             

water absorption, astm d696:<0.03 %          

limiting oxygen index, astm d2863: >95%           

upper service temperature: 500°f             

weather and chemical resistance: outstanding          

注射      额定值单位制      

螺筒后部温度       316到332°c    

螺筒中部温度       329到343°c    

螺筒前部温度       371°c  

射嘴温度       371°c  

加工（熔体）温度       343到399°c    

模具温度       149到260°c    

注塑温度       20.7到55.2mpa 

注射速度      慢   

合模力    6.9kn/cm²    