PC 6267防火（PC阻燃）德国科思创

拜耳物 PC 6267 性表

Physical Properties Metric English Comments

Mechanical Properties Metric English Comments

Electrical Properties Metric English Comments

Thermal Properties Metric English Comments

Processing Properties Metric English Comments

Descriptive Properties

Density	1.20 g/cc	0.0434 lb/in³	ISO 1183
	1.02 g/cc @Temperature 280 °C	0.0368 lb/in³ @Temperature 536 °F	Melt
Water Absorption	0.30 %	0.30 %	Similar to ISO 62
Moisture Absorption at Equilibrium	0.12 %	0.12 %	Similar to ISO 62
Linear Mold Shrinkage, Flow	0.0070 cm/cm	0.0070 in/in	parallel; ISO 294-4,2577
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ISO 294-4,2577
Melt Flow	19 g/10 min @Load 1.20 kg, Temperature 300 °C	19 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133
Tensile Strength, Yield	67.0 MPa	9720 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	Nominal; ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	ISO 527-1/-2
Tensile Modulus	2.45 GPa	355 ksi	ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
Impact	5000	5000	Puncture - maximum force (N); ISO 6603-2
	5900 @Temperature -30.0 °C	5900 @Temperature -22.0 °F	Puncture - maximum force (N); ISO 6603-2
Puncture Energy	50.0 J	36.9 ft-lb	ISO 6603-2
	55.0 J @Temperature -30.0 °C	40.6 ft-lb @Temperature -22.0 °F	ISO 6603-2
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.0 @Frequency 1.00e+6 Hz	3.0 @Frequency 1.00e+6 Hz	IEC 60250
	3.1 @Frequency 100 Hz	3.1 @Frequency 100 Hz	IEC 60250
Dielectric Strength	34.0 kV/mm	864 kV/in	IEC 60243-1
Dissipation Factor	0.00080 @Frequency 100 Hz	0.00080 @Frequency 100 Hz	IEC 60250
	0.0090 @Frequency 1.00e+6 Hz	0.0090 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	225 V	225 V	IEC 60112
CTE, linear, Parallel to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359-1/-2
Specific Heat Capacity	1.70 J/g-°C	0.406 BTU/lb-°F	Melt
Thermal Conductivity	0.173 W/m-K	1.20 BTU-in/hr-ft²-°F	Melt
Deflection Temperature at 0.46 MPa (66 psi)	134 °C	273 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	122 °C	252 °F	ISO 75-1/-2
Vicat Softening Point	144 °C	291 °F	50°C/h 50N; ISO 306
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
Oxygen Index	35 %	35 %	ISO 4589-1/-2
Melt Temperature	280 °C	536 °F	Injection Molding; ISO 294
	280 - 320 °C	536 - 608 °F
Mold Temperature	80.0 °C	176 °F	Injection Molding; ISO 10724
	80.0 - 120 °C	176 - 248 °F
Ejection Temperature	130 °C	266 °F
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294
Availability	Asia Pacific
	Europe
	India
	Near East/Africa
	North America
	South and Central America
Eff. thermal diffusivity (m²/s)	1E-07
Feature	Light stabilised or stable to light
	Release agent
	U.V. stabilised or stable to weather
Form	Pellets
Process	Injection Molding
UL recognition	UL\l1.5\n
	UL\lh\n