欧K膨胀玻化微珠 松脂岩矿砂

名称

name

原材料

raw material

物理性能

physical properties

在砂浆中的应用

application in mortar

膨胀珍

珠岩

expanded perlite

珍珠岩

perlite

1. 容重轻

（60～80kg/m³）

2．吸水率极大

3．颗粒强度低

4．导热系数小

1. low density

2.high water absorption

3.low particle strength

4.low heat conductivity

1．不规则与毛絮状的外形，容易在砂浆搅拌过程中产生阻力，和易性极差。

1. irregular and floccus, easy to make resistance while mixing, bad workability

2．容重轻，颗粒强度低，本身有较好的热工性能，但在砂浆搅拌过程中容易破碎，会很大程度降低其热工性能

2. low density, low particle strength, good thermal property itself, but break easily while mixing, and reduce thermal property.

3．吸水率大，使得砂浆的需水量增加，破坏了砂浆的凝固周期，使得砂浆的力学性能大大降低，极易产生空鼓、开裂，严重影响整个保温系统的热工性能和耐久性。

3. high water absorption, which increase mortar water demand, degrade its mechanical property significantly, then easy to have hollowing and craze, has a strong impact on the thermal property and durability.

闭孔珍珠岩

hole-close perlite

珍珠岩

perlite

1. 容重大

（120～180kg/m³）

2．吸水率较大

3．颗粒强度较大

4．导热系数大

1. high density

（120～180kg/m³）

2. high water absorption

3.high particle strength

4.high heat conductivity

1．不规则的外形，在砂浆中易产生阻力，和易性差，搅拌时间长，造成其在砂浆中不易分布均匀，容易造成应力集中，引起空鼓、开裂，大大降低了砂浆的力学性能和热工性能，也影响到保温层的使用寿命。

1. irregular shape makes it easy to produce resistance, low workability, long mixing time, makes it unevenly distributed in the mortar, which will easy cause stress concentration, hollowing and cracking, reduce mechanical property and thermal property greatly, also has impact on the insulation layer service life.

2．容量大，导热系数较差，在砂浆中必须增加轻骨料掺加比列方能满足热工性能标准要求，轻骨料掺加量的增加必然会降低砂浆的力学性能或增加胶凝材料成本。

2. high capacity with bad heat conductivity, need to increase light aggregate to meet the thermal property re, but adding light aggregate will reduce mortar mechanical property and increase gelled materials cost.

3．吸水率较大，在应用过程中会出现上述膨胀珍珠岩同样的问题，不过在各项指标上要优于膨胀珍珠岩。

3. high water absorption, will have similar problems as expanded perlite while using, but have better performance than expanded perlite.

膨胀玻化微珠

expanded and vitrified small ball

松脂岩

perlite

1.容重轻（80～120kg/m³）

2．吸水率小

3．颗粒强度较大

4．导热系数小

1. low density

（80～120kg/m³）

2.low water absorption

3.high particle strength

4.low heat conductivity

1．球状颗粒，表面玻化，在砂浆搅拌工程中流动性好，和易性佳，能在短时间内搅拌均匀，降低了砂浆在干湿搅拌过程中的骨料破碎，有稳定的热工性能与力学性能。

1. spherical particle, surface vitrified, good fluidity while mixing, good workability, mixed evenly shortly, then reduce the aggregate broke when dry-wet mixing, good thermal property and mechanical property.

2．容量轻，导热系数低

2. low density, light weight, low heat conductivity

3．吸水率小，很容易在砂浆中得到控制，收缩率小，不空鼓开裂，有稳定的热工性能与力学性能，并且也相对提高了砂浆的使用寿命。

3. low water absorption, easily controlled in mortar, low shrinkage, no hollowing and cracking, stable thermal property and mechanical property, increase the mortar service life.

项目item

i 类

ii 类

iii 类

堆积密度/kg/m³
bulk density

<80

<80～120

> 120

筒压强度/kpa
cylindrical compress strength

≥50

≥150

≥200

导热系数/w/(m·k)平均温度25℃
heat conductivity
average temperature 25℃

≤0.043

≤0.048

≤0.070

体积吸水率/%
volatile water absorption

≤45

体积漂浮率/%
volume floating rate

≥80

表面玻化闭孔率/%
surface vitrified close cell content

≥80